Typical Tensile Properties
| As welded | |||
| Elongation | Tensile Strength | Yield Strength | 保护气体 |
| 30 % | 610 MPa | 520 MPa | ISO |
| - | - | - | AWS |
夏比V型缺口冲击性能
| As welded | ||
| Impact Value | Testing Temperature | 保护气体 |
| 100 J | -50 °C | ISO |
焊缝金属分析
| Mn | ||||
| Mn | Cu | C | Si | Ni |
| 1.1 % | - | - | - | - |
| Cu | ||||
| Mn | Cu | C | Si | Ni |
| - | 0.4 % | - | - | - |
| C | ||||
| Mn | Cu | C | Si | Ni |
| - | - | 0.06 % | - | - |
| Si | ||||
| Mn | Cu | C | Si | Ni |
| - | - | - | 0.4 % | - |
| Ni | ||||
| Mn | Cu | C | Si | Ni |
| - | - | - | - | 0.7 % |
熔敷数据
| Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
| 59 sec | 0.62 kg | 66.0 | 80-115 A | 0.90 kg/h | 21 V | 2.5 x 350 mm |
| 68 sec | 0.62 kg | 43 | 100-150 A | 1.2 kg/h | 23 V | 3.2 x 350 mm |
| 90 sec | 0.66 kg | 30.5 | 100-150 A | 1.30 kg/h | 22 V | 3.2 x 450 mm |
| 100 sec | 0.68 kg | 20.0 | 130-200 A | 1.80 kg/h | 23 V | 4.0 x 450 mm |
| 106 sec | 0.70 kg | 13.5 | 190-280 A | 2.60 kg/h | 27 V | 5.0 x 450 mm |