点击图片查看原图
德国斯坦因MEGAFIL- A 760 M耐磨药芯焊丝
MEGAFIL- A 760 M metal cored T Fe 4 55-65 HRC
MEGAFIL- A 261 M metal cored TZ Fe 8 55-65 HRC
MEGAFIL- A 13-4 M metal cored TZ Fe 7 250-450 HB
MEGAFIL- 220 M metal cored TZ Fe 9 40-50 HRC
MEGAFIL- A 730 B basic T Fe 1 225-375 HB
MEGAFIL- A 740 B basic T Fe 2 375-450 HB
MEGAFIL- A 750 B basic T Fe 6 45-55 HRC
MEGAFIL- A 760 B basic T Fe 4 55-65 HRC
MEGAFIL- A 547 ×× basic TZ Fe 7 45-55 HRC
MEGAFIL- A 861 M metal cored T Fe 8 50-65 HRC
MEGAFIL- A 862 M metal cored TZ Fe 14 45-60 HRC
MEGAFIL- A 863 M metal cored TZ Fe 15 55-65 HRC
MEGAFIL- A 864 M metal cored T Fe 13 55-65 HRC
MEGAFIL- A 867 M metal cored TZ Fe 16 60-70 HRC
Wire type Type of slag EN 14700 Range of Hardness
MEGAFIL- A 730 M metal cored T Fe 1 225-375 HB
MEGAFIL- A 740 M metal cored T Fe 2 375-450 HB
MEGAFIL- A 750 M metal cored T Fe 6 45-55 HRC
MEGAFIL- A 760 M metal cored T Fe 4 55-65 HRC
MEGAFIL- A 261 M metal cored TZ Fe 8 55-65 HRC
MEGAFIL- A 13-4 M metal cored TZ Fe 7 250-450 HB
KSW-41
KSW-411
适用于高张力结构钢之接合；可用于旋窑胎环、环齿轮、驱动小齿轮及结构之焊接
KSW-42
KSW-312
适用于不明成份钢材、异种钢之接合；不会产生裂纹可用于传动轴磨损之堆 焊；高碳钢、高合金铸钢之接合；机械箱体、齿轮及钢制零件之补焊
KSW-45
KSW-303
奥氏体锰钢的接合级奥斯体锰钢与碳钢之接合；高合金结构钢之接合；亦可 用于硬面堆焊之中介层
KSW-65
KSW-605
此合金为具工作硬化之奥氏体堆焊层特别适用在高冲击或做为硬面堆焊的中介层；可使用于挖土机斗齿、推土机刀叶侧板、破碎机壳罩、链运机链条连接片、履带块等中介层堆焊
KSW-60
KSW-625
此堆焊合金具高度可加工性、及高韧性；适用于需承受高压及高冲击之备件 补焊；可用于旋窑支撑辊、环齿轮、小齿轮之补焊
KSW-61
KSW-626
此合金为奥氏体碳化铬之堆焊层；具有极佳耐磨耗性；特别适用在立磨辊 皮、磨盘衬板、螺旋输送机及破碎机Mantle及颚式破碎机颚板之堆焊
-
KSW-628
高耐磨性碳化铌、铬硬面堆焊；硬度可达HRC60-64
KSW-66
KSW-645
此合金为麻田散体碳化钛之堆焊层，适用于高应力形态之磨耗及大颗粒剥离 之磨耗，可使用于破碎机Mantle、双辊式破碎机辊、锤式破碎机锤头及滚压 机之硬面堆焊；硬度可达HRC56-58
KSW-69
KSW-629
此合金为高耐磨性多碳化物硬面堆焊对于各种形态之磨耗具极佳之耐磨耗性； 亦可使用于温度650℃之高温环境；特别适用在喷煤管前端及旋窑出口等高 温区；硬度可达HRC63—67
抗拉强度520N／mm2 延伸率22%
抗拉强度660N／mm2 延伸率20% Min
抗拉强度590N／mm2 延伸率30%Min
硬度HRC 18-24工作硬化后可达HRC 45-50
硬度HRC29-35
硬度可达HRC60-64